Highly effective stabilizer

ABSTRACT

A stabilizer composition containing 
     (I) a compound of the formula (I) 
                         
and
 
(II) a compound of the formula (II)
 
                         
wherein
 
the radicals R 1  independently of one another are C 1 -C 18  alkyl or C 3 -C 12  cycloalkyl;
 
the radicals X 1  independently of one another are hydrogen, C 1 -C 18  alkyl, C 3 -C 12  cycloalkyl or a group of the formula (III-I);
 
                         
the radicals X 2  independently of one another are hydrogen, C 1 -C 18  alkyl, C 3 -C 12  cycloalkyl or a group of the formula (III-II);
 
                         
and Y 1  is C 2 -C 12  alkylene.

The present invention relates to a stabilizer composition containing twospecific sterically hindered amine compounds, an organic materialsubject to degradation induced by light, heat or oxidation containingsaid stabilizer composition and the use of said stabilizer compositionas well as to particular polymers containing only one stericallyhindered amine compound of said stabilizer composition.

The stabilizer composition according to the present invention isparticularly useful as light stabilizer in plastic applications,typically polyolefin applications, used in agriculture and characterizedby high levels of contamination from chemicals (e.g. sulfur or chlorinecontaining compounds) used in the agronomic practice during soildisinfection and growth of the crops.

In more detail, the present invention relates to a stabilizercomposition containing

(I) a compound of the formula (I)

and

(II) a compound of the formula (II)

wherein

the radicals R₁ independently of one another are C₁-C₁₈ alkyl or C₃-C₁₂cycloalkyl;

the radicals X₁ independently of one another are hydrogen, C₁-C₁₈ alkyl,C₃-C₁₂ cycloalkyl or a group of the formula (III-I);

the radicals X₂ independently of one another are hydrogen, C₁-C₁₈ alkyl,C₃-C₁₂ cycloalkyl or a group of the formula (III-II);

and Y₁ is C₂-C₁₂ alkylene.

Examples of C₁-C₁₈ alkyl are methyl, ethyl, propyl, isopropyl, n-butyl,sec-butyl, isobutyl, tert-butyl, 2-ethylbutyl, n-pentyl, isopentyl,1-methyl-pentyl, 1,3-dimethyl¬butyl, n-hexyl, 1-methyl¬hexyl, n-heptyl,isoheptyl, 1,1,3,3-tetra¬methyl¬butyl, 1-methyl¬heptyl, 3-methyl¬heptyl,n-octyl, 2-ethyl¬hexyl, 1,1,3-tri¬methyl-hexyl,1,1,3,3-tetra¬methyl¬pentyl, nonyl, decyl, undecyl, 1-methyl¬undecyl,dodecyl, 1,1,3,3,5,5-hexa¬methyl¬hexyl, tridecyl, tetradecyl,pentadecyl, hexadecyl, heptadecyl and octadecyl.

Examples of C₃-C₁₂ cycloalkyl are cyclopentyl, cyclohexyl, cycloheptyl,cyclooctyl and cyclododecyl.

Examples of C₂-C₁₂ alkylene are ethylene, propylene, trimethylene,tetramethylene, pentamethylene, 2,2-dimethyltrimethylene andhexamethylene.

A preferred embodiment relates to a stabilizer composition wherein

the radicals R₁ independently of one another are C₁-C₁₂ alkyl or C₃-C₆cycloalkyl;

the radicals X₁ independently of one another are hydrogen, C₁-C₁₂ alkylor C₃-C₆ cycloalkyl; the radicals X₂ independently of one another arehydrogen, C₁-C₁₂ alkyl or C₃-C₆ cycloalkyl; and Y₁ is C₂-C₆ alkylene.

R₁, X₁ and X₂ are preferably C₁-C₄ alkyl and Y₁ is preferablyhexamethylene.

According to a particularly preferred embodiment R₁ is n-propyl, X₁ andX₂ are n-butyl and Y₁ is hexamethylene.

In the stabilizer compositions according to the present invention theweight ratio of the compound of the formula (I) to the compound of theformula (II) is for example 1:20 to 20:1, preferably 1:10 to 10:1, inparticular 1:5 to 5:1. Further examples of a suitable weight ratio are3:1 to 1:3 and 2:1 to 1:2.

The compounds of the formulae (I) and (II) are known and can be preparedin analogy to processes known to those skilled in the art. The compoundsof the formula (I) can be prepared for example in analogy to the methoddescribed in WO-A-2011/029,744 (equivalent to U.S. Pat. No. 8,895,647which is incorporated by reference herein) and the compounds of theformula (II) can be prepared for example in analogy to the methoddescribed in EP-A-292,437 (equivalent to U.S. Pat. Nos. 4,997,938 and5,116,893 which are incorporated by reference herein).

A further embodiment of the present invention relates to a compositioncontaining (A) an organic material subject to degradation induced bylight, heat or oxidation, preferably a polyolefin,

and

(B) a stabilizer composition as defined above.

Examples of component (A) are

1. Polymers of monoolefins and diolefins, for example polypropylene,polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene,polyvinylcyclohexane, polyisoprene or polybutadiene, as well as polymersof cycloolefins, for instance of cyclopentene or norbornene,polyethylene (which optionally can be crosslinked), for example highdensity polyethylene (HDPE), high density and high molecular weightpolyethylene (HDPE-HMW), high density and ultrahigh molecular weightpolyethylene (HDPE-UHMW), medium density polyethylene (MDPE), lowdensity polyethylene (LDPE), linear low density polyethylene (LLDPE),(VLDPE) and (ULDPE).

Polyolefins, i.e. the polymers of monoolefins exemplified in thepreceding paragraph, preferably polyethylene and polypropylene, can beprepared by different, and especially by the following, methods:

-   -   a) radical polymerisation (normally under high pressure and at        elevated temperature).    -   b) catalytic polymerisation using a catalyst that normally        contains one or more than one metal of groups IVb, Vb, VIb or        VIII of the Periodic Table. These metals usually have one or        more than one ligand, typically oxides, halides, alcoholates,        esters, ethers, amines, alkyls, alkenyls and/or aryls that may        be either π- or σ-coordinated. These metal complexes may be in        the free form or fixed on substrates, typically on activated        magnesium chloride, titanium(Ill) chloride, alumina or silicon        oxide. These catalysts may be soluble or insoluble in the        polymerisation medium. The catalysts can be used by themselves        in the polymerisation or further activators may be used,        typically metal alkyls, metal hydrides, metal alkyl halides,        metal alkyl oxides or metal alkyloxanes, said metals being        elements of groups Ia, IIa and/or IIa of the Periodic Table. The        activators may be modified conveniently with further ester,        ether, amine or silyl ether groups. These catalyst systems are        usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta),        TNZ (DuPont), metallocene or single site catalysts (SSC).

2. Mixtures of the polymers mentioned under 1), for example mixtures ofpolypropylene with polyisobutylene, polypropylene with polyethylene (forexample PP/HDPE, PP/LDPE) and mixtures of different types ofpolyethylene (for example LDPE/HDPE).

3. Copolymers of monoolefins and diolefins with each other or with othervinyl monomers, for example ethylene/propylene copolymers, linear lowdensity polyethylene (LLDPE) and mixtures thereof with low densitypolyethylene (LDPE), propylene/but-1-ene copolymers,propylene/isobutylene copolymers, ethylene/but-1-ene copolymers,ethylene/hexene copolymers, ethylene/methylpentene copolymers,ethylene/heptene copolymers, ethylene/octene copolymers,ethylene/vinylcyclohexane copolymers, ethylene/cycloolefin copolymers(e.g. ethylene/norbornene like COC), ethylene/1-olefins copolymers,where the 1-olefin is generated in-situ; propylene/butadiene copolymers,isobutylene/isoprene copolymers, ethylene/vinylcyclohexene copolymers,ethylene/alkyl acrylate copolymers, ethylene/alkyl methacrylatecopolymers, ethylene/vinyl acetate copolymers or ethylene/acrylic acidcopolymers and their salts (ionomers) as well as terpolymers of ethylenewith propylene and a diene such as hexadiene, dicyclopentadiene orethylidene-norbornene; and mixtures of such copolymers with one anotherand with polymers mentioned in 1) above, for examplepolypropylene/ethylenepropylene copolymers, LDPE/ethylene-vinyl acetatecopolymers (EVA), LDPE/ethylene-acrylic acid copolymers (EAA),LLDPE/EVA, LLDPE/EAA and alternating or random polyalkylene/carbonmonoxide copolymers and mixtures thereof with other polymers, forexample polyamides.

4. Hydrocarbon resins (for example C₅-C₉) including hydrogenatedmodifications thereof (e.g. tackifiers) and mixtures of polyalkylenesand starch.

Homopolymers and copolymers from 1.)-4.) may have any stereostructureincluding syndiotactic, isotactic, hemi-isotactic or atactic; whereatactic polymers are preferred. Stereoblock polymers are also included.

5. Polystyrene, poly(p-methylstyrene), poly(α-methylstyrene).

6. Aromatic homopolymers and copolymers derived from vinyl aromaticmonomers including styrene, α-methylstyrene, all isomers of vinyltoluene, especially p-vinyltoluene, all isomers of ethyl styrene, propylstyrene, vinyl biphenyl, vinyl naphthalene, and vinyl anthracene, andmixtures thereof. Homopolymers and copolymers may have anystereostructure including syndiotactic, isotactic, hemi-isotactic oratactic; where atactic polymers are preferred. Stereoblock polymers arealso included.

6a. Copolymers including aforementioned vinyl aromatic monomers andcomonomers selected from ethylene, propylene, dienes, nitriles, acids,maleic anhydrides, maleimides, vinyl acetate and vinyl chloride oracrylic derivatives and mixtures thereof, for example styrene/butadiene,styrene/acrylonitrile, styrene/ethylene (interpolymers), styrene/alkylmethacrylate, styrene/butadiene/alkyl acrylate, styrene/butadiene/alkylmethacrylate, styrene/maleic anhydride, styrene/acrylonitrile/methylacrylate; mixtures of high impact strength of styrene copolymers andanother polymer, for example a polyacrylate, a diene polymer or anethylene/propylene/diene terpolymer; and block copolymers of styrenesuch as styrene/butadiene/styrene, styrene/isoprene/styrene,styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene.

6b. Hydrogenated aromatic polymers derived from hydrogenation ofpolymers mentioned under 6.), especially includingpolycyclohexylethylene (PCHE) prepared by hydrogenating atacticpolystyrene, often referred to as polyvinylcyclohexane (PVCH).

6c. Hydrogenated aromatic polymers derived from hydrogenation ofpolymers mentioned under 6a.).

Homopolymers and copolymers may have any stereostructure includingsyndiotactic, isotactic, hemi-isotactic or atactic; where atacticpolymers are preferred. Stereoblock polymers are also included.

7. Graft copolymers of vinyl aromatic monomers such as styrene orα-methylstyrene, for example styrene on polybutadiene, styrene onpolybutadiene-styrene or polybutadiene-acrylonitrile copolymers; styreneand acrylonitrile (or methacrylonitrile) on polybutadiene; styrene,acrylonitrile and methyl methacrylate on polybutadiene; styrene andmaleic anhydride on polybutadiene; styrene, acrylonitrile and maleicanhydride or maleimide on polybutadiene; styrene and maleimide onpolybutadiene; styrene and alkyl acrylates or methacrylates onpolybutadiene; styrene and acrylonitrile on ethylene/propylene/dieneterpolymers; styrene and acrylonitrile on polyalkyl acrylates orpolyalkyl methacrylates, styrene and acrylonitrile on acrylate/butadienecopolymers, as well as mixtures thereof with the copolymers listed under6), for example the copolymer mixtures known as ABS, MBS, ASA or AESpolymers.

8. Halogen-containing polymers such as polychloroprene, chlorinatedrubbers, chlorinated and brominated copolymer of isobutylene-isoprene(halobutyl rubber), chlorinated or sulfochlorinated polyethylene,copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo-and copolymers, especially polymers of halogen-containing vinylcompounds, for example polyvinyl chloride, polyvinylidene chloride,polyvinyl fluoride, polyvinylidene fluoride, as well as copolymersthereof such as vinyl chloride/vinylidene chloride, vinyl chloride/vinylacetate or vinylidene chloride/vinyl acetate copolymers.

9. Polymers derived from α,β-unsaturated acids and derivatives thereofsuch as polyacrylates and polymethacrylates; polymethyl methacrylates,polyacrylamides and polyacrylonitriles, impact-modified with butylacrylate.

10. Copolymers of the monomers mentioned under 9) with each other orwith other unsaturated monomers, for example acrylonitrile/butadienecopolymers, acrylonitrile/alkyl acrylate copolymers,acrylonitrile/alkoxyalkyl acrylate or acrylonitrile/vinyl halidecopolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers.

11. Polymers derived from unsaturated alcohols and amines or the acylderivatives or acetals thereof, for example polyvinyl alcohol, polyvinylacetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate,polyvinyl butyral, polyallyl phthalate or polyallyl melamine; as well astheir copolymers with olefins mentioned in 1) above.

12. Homopolymers and copolymers of cyclic ethers such as polyalkyleneglycols, polyethylene oxide, polypropylene oxide or copolymers thereofwith bisglycidyl ethers.

13. Polyacetals such as polyoxymethylene and those polyoxymethyleneswhich contain ethylene oxide as a comonomer; polyacetals modified withthermoplastic polyurethanes, acrylates or MBS.

14. Polyphenylene oxides and sulfides, and mixtures of polyphenyleneoxides with styrene polymers or polyamides.

15. Polyurethanes derived from hydroxyl-terminated polyethers,polyesters or polybutadienes on the one hand and aliphatic or aromaticpolyisocyanates on the other, as well as precursors thereof.

16. Polyamides and copolyamides derived from diamines and dicarboxylicacids and/or from aminocarboxylic acids or the corresponding lactams,for example polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12,4/6, 12/12, polyamide 11, polyamide 12, aromatic polyamides startingfrom m-xylene diamine and adipic acid; polyamides prepared fromhexamethylenediamine and isophthalic or/and terephthalic acid and withor without an elastomer as modifier, for examplepoly-2,4,4,-trimethylhexamethylene terephthalamide or poly-m-phenyleneisophthalamide; and also block copolymers of the aforementionedpolyamides with polyolefins, olefin copolymers, ionomers or chemicallybonded or grafted elastomers; or with polyethers, e.g. with polyethyleneglycol, polypropylene glycol or polytetramethylene glycol; as well aspolyamides or copolyamides modified with EPDM or ABS; and polyamidescondensed during processing (RIM polyamide systems).

17. Polyureas, polyimides, polyamide-imides, polyetherimides,polyesterimides, polyhydantoins and polybenzimidazoles.

18. Polyesters derived from dicarboxylic acids and diols and/or fromhydroxycarboxylic acids or the corresponding lactones or lactides, forexample polyethylene terephthalate, polybutylene terephthalate,poly-1,4-dimethylolcyclohexane terephthalate, polyalkylene naphthalateand polyhydroxybenzoates as well as copolyether esters derived fromhydroxyl-terminated polyethers, and also polyesters modified withpolycarbonates or MBS. Copolyesters may comprise, for example—but arenot limited to—polybutylenesuccinate/terephtalate,polybutyleneadipate/terephthalate,polytetramethyleneadipate/terephthalate, polybutylensuccinate/adipate,polybutylensuccinate/carbonate, poly-3-hydroxybutyrate/octanoatecopolymer, poly-3-hydroxybutyrate/hexanoate/decanoate terpolymer.Furthermore, aliphatic polyesters may comprise, for example—but are notlimited to—the class of poly(hydroxyalkanoates), in particular,poly(propiolactone), poly(butyrolactone), poly(pivalolactone),poly(valerolactone) and poly(caprolactone), polyethylenesuccinate,polypropylenesuccinate, polybutylenesuccinate,polyhexamethylenesuccinate, polyethyleneadipate, polypropyleneadipate,polybutyleneadipate, polyhexamethyleneadipate, polyethyleneoxalate,polypropyleneoxalate, polybutyleneoxalate, polyhexamethyleneoxalate,polyethylenesebacate, polypropylenesebacate, polybutylenesebacate andpolylactic acid (PLA) as well as corresponding polyesters modified withpolycarbonates or MBS. The term “polylactic acid (PLA)” designates ahomo-polymer of preferably poly-L-lactide and any of its blends oralloys with other polymers; a co-polymer of lactic acid or lactide withother monomers, such as hydroxy-carboxylic acids, like for exampleglycolic acid, 3-hydroxy-butyric acid, 4-hydroxy-butyric acid,4-hydroxy-valeric acid, 5-hydroxy-valeric acid, 6-hydroxy-caproic acidand cyclic forms thereof; the terms “lactic acid” or “lactide” includeL-lactic acid, D-lactic acid, mixtures and dimers thereof, i.e.L-lactide, D-lactide, meso-lacide and any mixtures thereof.

19. Polycarbonates and polyester carbonates.

20. Polyketones.

21. Polysulfones, polyether sulfones and polyether ketones.

22. Crosslinked polymers derived from aldehydes on the one hand andphenols, ureas and melamines on the other hand, such asphenol/formaldehyde resins, urea/formaldehyde resins andmelamine/formaldehyde resins.

23. Drying and non-drying alkyd resins.

24. Unsaturated polyester resins derived from copolyesters of saturatedand unsaturated dicarboxylic acids with polyhydric alcohols and vinylcompounds as crosslinking agents, and also halogen-containingmodifications thereof of low flammability.

25. Crosslinkable acrylic resins derived from substituted acrylates, forexample epoxy acrylates, urethane acrylates or polyester acrylates.

26. Alkyd resins, polyester resins and acrylate resins crosslinked withmelamine resins, urea resins, isocyanates, isocyanurates,polyisocyanates or epoxy resins.

27. Crosslinked epoxy resins derived from aliphatic, cycloaliphatic,heterocyclic or aromatic glycidyl compounds, e.g. products of diglycidylethers of bisphenol A and bisphenol F, which are crosslinked withcustomary hardeners such as anhydrides or amines, with or withoutaccelerators.

28. Natural polymers such as cellulose, rubber, gelatin and chemicallymodified homologous derivatives thereof, for example cellulose acetates,cellulose propionates and cellulose butyrates, or the cellulose etherssuch as methyl cellulose; as well as rosins and their derivatives.

29. Blends of the aforementioned polymers (polyblends), for examplePP/EPDM, Polyamide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS,PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR,PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 andcopolymers, PA/HDPE, PA/PP, PA/PPO, PBT/PC/ABS or PBT/PET/PC.

30. Naturally occurring and synthetic organic materials which are puremonomeric compounds or mixtures of such compounds, for example mineraloils, animal and vegetable fats, oil and waxes, or oils, fats and waxesbased on synthetic esters (e.g. phthalates, adipates, phosphates ortrimellitates) and also mixtures of synthetic esters with mineral oilsin any weight ratios, typically those used as spinning compositions, aswell as aqueous emulsions of such materials.

31. Aqueous emulsions of natural or synthetic rubber, e.g. natural latexor latices of carboxylated styrene/butadiene copolymers.

The organic material is preferably selected from the group consisting oflow density polyethylene, high density polyethylene, ethylene-vinylacetate copolymer, ethylene-butyl acrylate copolymer, and polypropylenehomo- or copolymer.

The stabilizer composition according to the present invention may bepresent in the organic material to be stabilized in an amount ofpreferably 0.005 to 10% or 0.005 to 5%, in particular 0.01 to 2.5% or0.1 to 2%, relative to the weight of the organic material.

The individual components of the present stabilizer composition may beadded to the organic material to be stabilized either individually ormixed with one another. They can be added to a polymer before or duringthe polymerization or before the crosslinking.

The stabilizer composition according to the present invention or itsindividual components can be incorporated into the organic material tobe stabilized by known methods, for example before or during shaping orby applying the dissolved or dispersed stabilizer to the organicmaterial, if necessary with subsequent evaporation of the solvent. Thestabilizers can be added to the organic material in the form of apowder, granules or a masterbatch, which contains said stabilizers in,for example, a concentration of from 2.5 to 25% by weight.

EXAMPLES OF PROCESSING OR TRANSFORMATION OF THE MATERIALS STABILIZEDACCORDING TO THE PRESENT INVENTION ARE

Injection blow molding, extrusion, blow molding, rotomolding, in molddecoration (back injection), slush molding, injection molding,co-injection molding, forming, compression molding, pressing, filmextrusion (cast film; blown film), fiber spinning (woven, nonwoven),drawing (uniaxial, biaxial), annealing, deep drawing, calandering,mechanical transformation, sintering, coextrusion, coating, lamination,crosslinking (radiation, peroxide, silane), vapor deposition, weldtogether, glue, vulkanization, thermoforming, pipe extrusion, profileextrusion, sheet extrusion; sheet casting, spin coating, strapping,foaming, recycling/rework, extrusion coating, visbreaking (peroxide,thermal), fiber melt blown, spun bonded, surface treatment (coronadischarge, flame, plasma), sterilization (by gamma rays, electronbeams), cast polymerization (R&M process, RAM extrusion), gel-coating,tape extrusion, GMT-process, SMC-process, plastisol, and dipping (PVC,latex).

The stabilized material may additionally also contain variousconventional additives, for example:

1. Antioxidants

1.1. Alkylated monophenols, for example2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol,2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol,2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol,2-(X-methylcyclohexyl)-4,6-dimethylphenol,2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol,2,6-di-tert-butyl-4-methoxymethylphenol, nonylphenols which are linearor branched in the side chains, for example,2,6-di-nonyl-4-methylphenol,2,4-dimethyl-6-(1′-methylundec-1′-yl)phenol,2,4-dimethyl-6-(1′-methylheptadec-1′-yl)phenol,2,4-dimethyl-6-(1′-methyltridec-1′-yl)phenol and mixtures thereof.1.2. Alkylthiomethylphenols, for example2,4-dioctylthiomethyl-6-tert-butylphenol,2,4-dioctylthiomethyl-6-methylphenol,2,4-dioctylthiomethyl-6-ethylphenol,2,6-di-dodecylthiomethyl-4-nonylphenol.1.3. Hydroquinones and alkylated hydroquinones, for example2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone,2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyloxyphenol,2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole,3,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyphenylstearate, bis(3,5-di-tert-butyl-4-hydroxyphenyl) adipate.1.4. Tocopherols, for example α-tocopherol, β-tocopherol, γ-tocopherol,δ-tocopherol and mixtures thereof (vitamin E).1.5. Hydroxylated thiodiphenyl ethers, for example2,2′-thiobis(6-tert-butyl-4-methylphenol), 2,2′-thiobis(4-octylphenol),4,4′-thiobis(6-tert-butyl-3-methylphenol),4,4′-thiobis(6-tert-butyl-2-methylphenol),4,4′-thiobis(3,6-di-sec-amylphenol),4,4′-bis(2,6-dimethyl-4-hydroxyphenyl)disulfide.1.6. Alkylidenebisphenols, for example2,2′-methylenebis(6-tert-butyl-4-methylphenol),2,2′-methylenebis(6-tert-butyl-4-ethylphenol),2,2′-methylenebis[4-methyl-6-(α-methylcyclohexyl)phenol],2,2′-methylenebis(4-methyl-6-cyclohexylphenol),2,2′-methylenebis(6-nonyl-4-methylphenol),2,2′-methylenebis(4,6-di-tert-butylphenol),2,2′-ethylidenebis(4,6-di-tert-butylphenol),2,2′-ethylidenebis(6-tert-butyl-4-isobutylphenol),2,2′-methylenebis[6-(α-methylbenzyl)-4-nonylphenol],2,2′-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol],4,4′-methylenebis(2,6-di-tert-butylphenol),4,4′-methylenebis(6-tert-butyl-2-methylphenol),1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)butane,2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol,1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane,1,1-bis(5-tert-butyl-4-hydroxy-2-methyl-phenyl)-3-n-dodecylmercaptobutane,ethylene glycol bis[3,3-bis(3′-tert-butyl-4′-hydroxyphenyl)butyrate],bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadiene,bis[2-(3′-tert-butyl-2′-hydroxy-5′-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate,1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane,2,2-bis(3,5-di-tert-butyl-4-hydroxyphenyl)propane,2,2-bis(5-tert-butyl-4-hydroxy2-methylphenyl)-4-n-dodecylmercaptobutane,1,1,5,5-tetra-(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane.1.7. O-, N- and S-benzyl compounds, for example3,5,3′,5′-tetra-tert-butyl-4,4′-dihydroxydibenzyl ether,octadecyl-4-hydroxy-3,5-dimethylbenzylmercaptoacetate,tridecyl-4-hydroxy-3,5-di-tert-butylbenzylmercaptoacetate,tris(3,5-di-tert-butyl-4-hydroxybenzyl)amine,bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithioterephthalate,bis(3,5-di-tert-butyl-4-hydroxybenzyl)sulfide,isooctyl-3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate.1.8. Hydroxybenzylated malonates, for exampledioctadecyl-2,2-bis(3,5-di-tert-butyl-2-hydroxybenzyl)malonate,di-octadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonate,di-dodecylmercaptoethyl-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate,bis[4-(1,1,3,3-tetramethylbutyl)phenyl]-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate.1.9. Aromatic hydroxybenzyl compounds, for example1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene,1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene,2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol.1.10. Triazine compounds, for example2,4-bis(octylmercapto)-6-(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine,2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyanilino)-1,3,5-triazine,2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,3,5-triazine,2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine,1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate,1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate,2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1,3,5-triazine,1,3,5-tris(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexahydro-1,3,5-triazine,1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl)isocyanurate.1.11. Benzylphosphonates, for exampledimethyl-2,5-di-tert-butyl-4-hydroxybenzylphosphonate,diethyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonate,di-octadecyl3,5-di-tert-butyl-4-hydroxybenzylphosphonate,dioctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, thecalcium salt of the monoethyl ester of3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid.1.12. Acylaminophenols, for example 4-hydroxylauranilide,4-hydroxystearanilide, octylN-(3,5-di-tert-butyl-4-hydroxyphenyl)carbamate.1.13. Esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid withmono- or polyhydric alcohols, e.g. with methanol, ethanol, n-octanol,i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol,1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethyleneglycol, triethylene glycol, pentaerythritol,tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,trimethylolpropane,4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.1.14. Esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acidwith mono- or polyhydric alcohols, e.g. with methanol, ethanol,n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol,ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethyleneglycol, diethylene glycol, triethylene glycol, pentaerythritol,tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,trimethylolpropane,4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane;3,9-bis[2-{3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane.1.15. Esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid withmono- or polyhydric alcohols, e.g. with methanol, ethanol, octanol,octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol,1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethyleneglycol, triethylene glycol, pentaerythritol,tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,trimethylolpropane,4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.1.16. Esters of 3,5-di-tert-butyl-4-hydroxyphenyl acetic acid with mono-or polyhydric alcohols, e.g. with methanol, ethanol, octanol,octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol,1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethyleneglycol, triethylene glycol, pentaerythritol,tris(hydroxyethyl)isocyanurate, N,N′-bis(hydroxyethyl)oxamide,3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol,trimethylolpropane,4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.1.17. Amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid e.g.N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide,N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)trimethylenediamide,N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazide,N,N′-bis[2-(3-[3,5-di-tert-butyl-4-hydroxyphenyl]propionyloxy)ethyl]oxamide(Naugard® XL-1, supplied by Uniroyal).1.18. Ascorbic acid (vitamin C)1.19. Aminic antioxidants, for exampleN,N′-di-isopropyl-p-phenylenediamine,N,N′-di-sec-butyl-p-phenylenediamine,N,N′-bis(1,4-dimethylpentyl)-p-phenylenediamine,N,N′-bis(1-ethyl-3-methylpentyl)-p-phenylenediamine,N,N′-bis(1-methylheptyl)-p-phenylenediamine,N,N′-dicyclohexyl-p-phenylenediamine, N,N′-diphenyl-p-phenylenediamine,N,N′-bis(2-naphthyl)-p-phenylenediamine,N-isopropyl-N′-phenyl-p-phenylenediamine,N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine,N-(1-methylheptyl)-N′-phenyl-p-phenylenediamine,N-cyclohexyl-N′-phenyl-p-phenylenediamine,4-(p-toluenesulfamoyl)diphenylamine,N,N′-dimethyl-N,N′-di-sec-butyl-p-phenylenediamine, diphenylamine,N-allyldiphenylamine, 4-isopropoxydiphenylamine,N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine,N-phenyl-2-naphthylamine, octylated diphenylamine, for examplep,p′-di-tert-octyldiphenylamine, 4-n-butylaminophenol,4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylaminophenol,4-octadecanoylaminophenol, bis(4-methoxyphenyl)amine,2,6-di-tert-butyl-4-dimethylaminomethylphenol,2,4′-diaminodiphenylmethane, 4,4′-diaminodiphenylmethane,N,N,N′,N′-tetramethyl-4,4′-diaminodiphenylmethane,1,2-bis[(2-methylphenyl)amino]ethane, 1,2-bis(phenylamino)propane,(o-tolyl)biguanide, bis[4-(1′,3′-dimethylbutyl)phenyl]amine,tert-octylated N-phenyl-1-naphthylamine, a mixture of mono- anddialkylated tert-butyl/tert-octyldiphenylamines, a mixture of mono- anddialkylated nonyldiphenylamines, a mixture of mono- and dialkylateddodecyldiphenylamines, a mixture of mono- and dialkylatedisopropyl/isohexyldiphenylamines, a mixture of mono- and dialkylatedtert-butyldiphenylamines, 2,3-dihydro-3,3-dimethyl-4H-1,4-benzothiazine,phenothiazine, a mixture of mono- and dialkylatedtert-butyl/tert-octylphenothiazines, a mixture of mono- and dialkylatedtert-octyl-phenothiazines, N-allylphenothiazine,N,N,N′,N′-tetraphenyl-1,4-diaminobut-2-ene.2. UV absorbers and light stabilizers2.1. 2-(2′-Hydroxyphenyl)benzotriazoles, for example2-(2′-hydroxy-5′-methylphenyl)-benzotriazole,2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)benzotriazole,2-(5′-tert-butyl-2′-hydroxyphenyl)benzotriazole,2-(2′-hydroxy-5′-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole,2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)-5-chloro-benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-methylphenyl)-5-chloro-benzotriazole,2-(3′-sec-butyl-5′-tert-butyl-2′-hydroxyphenyl)benzotriazole,2-(2′-hydroxy-4′-octyloxyphenyl)benzotriazole,2-(3′,5′-di-tert-amyl-2′-hydroxyphenyl)benzotriazole,2-(3′,5′-bis-(α,α-dimethylbenzyl)-2′-hydroxyphenyl)benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)-5-chloro-benzotriazole,2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)-carbonylethyl]-2′-hydroxyphenyl)-5-chloro-benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)phenyl)-5-chloro-benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)phenyl)benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)benzotriazole,2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)benzotriazole,2-(3′-dodecyl-2′-hydroxy-5′-methylphenyl)benzotriazole,2-(3′-tert-butyl-2′-hydroxy-5′-(2-isooctyloxycarbonylethyl)phenylbenzotriazole,2,2′-methylene-bis[4-(1,1,3,3-tetramethylbutyl)-6-benzotriazole-2-ylphenol];the transesterification product of2-[3′-tert-butyl-5′-(2-methoxycarbonylethyl)-2′-hydroxyphenyl]-2H-benzotriazolewith polyethylene glycol 300; [R—CH₂CH₂—COO—CH₂CH₂

₂, where R=3′-tert-butyl-4′-hydroxy-5′-2H-benzotriazol-2-ylphenyl,2-[2′-hydroxy-3′-(α,α-dimethylbenzyl)-5′-(1,1,3,3-tetramethylbutyl)-phenyl]benzotriazole;2-[2′-hydroxy-3′-(1,1,3,3-tetramethylbutyl)-5′-(α,α-dimethylbenzyl)-phenyl]benzotriazole.2.2. 2-Hydroxybenzophenones, for example the 4-hydroxy, 4-methoxy,4-octyloxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy, 4,2′,4′-trihydroxyand 2′-hydroxy-4,4′-dimethoxy derivatives.2.3. Esters of substituted and unsubstituted benzoic acids, for example4-tert-butylphenyl salicylate, phenyl salicylate, octylphenylsalicylate, dibenzoyl resorcinol, bis(4-tert-butylbenzoyl)resorcinol,benzoyl resorcinol, 2,4-di-tert-butylphenyl3,5-di-tert-butyl-4-hydroxybenzoate, hexadecyl3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl3,5-di-tert-butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl3,5-di-tert-butyl-4-hydroxybenzoate.2.4. Acrylates, for example ethyl α-cyano-β,β-diphenylacrylate, isooctylα-cyano-β,β-diphenylacrylate, methyl α-carbomethoxycinnamate, methylα-cyano-β-methyl-p-methoxycinnamate, butylα-cyano-β-methyl-p-methoxy-cinnamate, methylα-carbomethoxy-p-methoxycinnamate,N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline, neopentyltetra(α-cyano-β,β-diphenylacrylate.2.5. Nickel compounds, for example nickel complexes of2,2′-thio-bis[4-(1,1,3,3-tetramethylbutyl)phenol], such as the 1:1 or1:2 complex, with or without additional ligands such as n-butylamine,triethanolamine or N-cyclohexyldiethanolamine, nickeldibutyldithiocarbamate, nickel salts of the monoalkyl esters, e.g. themethyl or ethyl ester, of 4-hydroxy-3,5-di-tert-butylbenzylphosphonicacid, nickel complexes of ketoximes, e.g. of2-hydroxy-4-methylphenylundecylketoxime, nickel complexes of1-phenyl-4-lauroyl-5-hydroxypyrazole, with or without additionalligands.2.6. Sterically hindered amines, for example carbonic acidbis(1-undecyloxy-2,2,6,6-tetramethyl-4-piperidyl)ester,bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate,bis(2,2,6,6-tetramethyl-4-piperidyl)succinate,bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacate,bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidyl)sebacate,bis(1,2,2,6,6-pentamethyl-4-piperidyl)n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinicacid, linear or cyclic condensates ofN,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and4-tert-octylamino-2,6-dichloro-1,3,5-triazine,tris(2,2,6,6-tetramethyl-4-piperidyl)nitrilotriacetate,tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylate,1,1′-(1,2-ethanediyl)-bis(3,3,5,5-tetramethylpiperazinone),4-benzoyl-2,2,6,6-tetramethylpiperidine,4-stearyloxy-2,2,6,6-tetramethylpiperidine,bis(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)-malonate,3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione,bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl)sebacate,bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl)succinate, linear or cycliccondensates ofN,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and4-morpholino-2,6-dichloro-1,3,5-triazine, the condensate of2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazineand 1,2-bis(3-aminopropylamino)ethane, the condensate of2-chloro-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazineand 1,2-bis(3-aminopropylamino)ethane,8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione,3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione,3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione, amixture of 4-hexadecyloxy- and4-stearyloxy-2,2,6,6-tetramethylpiperidine, a condensate ofN,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and4-cyclohexylamino-2,6-dichloro-1,3,5-triazine, a condensate of1,2-bis(3-aminopropylamino)ethane and 2,4,6-trichloro-1,3,5-triazine aswell as 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS Reg. No.[136504-96-6]); a condensate of 1,6-hexanediamine and2,4,6-trichloro-1,3,5-triazine as well as N,N-dibutylamine and4-butylamino-2,2,6,6-tetramethylpiperidine (CAS Reg. No. [192268-64-7]);N-(2,2,6,6-tetramethyl-4-piperidyl)-n-dodecylsuccinimide,N-(1,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecylsuccinimide,2-undecyl-7,7,9,9-tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4,5]decane, areaction product of7,7,9,9-tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro-[4,5]decaneand epichlorohydrin,1,1-bis(1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)-2-(4-methoxyphenyl)ethene,N,N′-bis-formyl-N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine,a diester of 4-methoxymethylenemalonic acid with1,2,2,6,6-pentamethyl-4-hydroxypiperidine,poly[methylpropyl-3-oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]siloxane, areaction product of maleic acid anhydride-α-olefin copolymer with2,2,6,6-tetramethyl-4-aminopiperidine or1,2,2,6,6-pentamethyl-4-aminopiperidine,2,4-bis[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidine-4-yl)-N-butylamino]-6-(2-hydroxyethyl)amino-1,3,5-triazine,1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine,5-(2-ethylhexanoyl)oxymethyl-3,3,5-trimethyl-2-morpholinone, Sanduvor(Clariant; CAS Reg. No. 106917-31-1],5-(2-ethylhexanoyl)oxymethyl-3,3,5-trimethyl-2-morpholinone, thereaction product of2,4-bis[(1-cyclohexyloxy-2,2,6,6-piperidine-4-yl)butylamino]-6-chloro-s-triazinewith N,N′-bis(3-aminopropyl)ethylenediamine),1,3,5-tris(N-cyclohexyl-N-(2,2,6,6-tetramethylpiperazine-3-one-4-yl)amino)-s-triazine,1,3,5-tris(N-cyclohexyl-N-(1,2,2,6,6-pentamethylpiperazine-3-one-4-yl)amino)-s-triazine.2.7. Oxamides, for example 4,4′-dioctyloxyoxanilide,2,2′-diethoxyoxanilide, 2,2′-dioctyloxy-5,5′-di-tert-butoxanilide,2,2′-didodecyloxy-5,5′-di-tert-butoxanilide, 2-ethoxy-2′-ethyloxanilide,N,N′-bis(3-dimethylaminopropyl)oxamide,2-ethoxy-5-tert-butyl-2′-ethoxanilide and its mixture with2-ethoxy-2′-ethyl-5,4′-di-tert-butoxanilide, mixtures of o- andp-methoxy-disubstituted oxanilides and mixtures of o- andp-ethoxy-disubstituted oxanilides.2.8. 2-(2-Hydroxyphenyl)-1,3,5-triazines, for example2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine,2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2,4-bis(2-hydroxy-4-propyloxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine,2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-1,3,5-triazine,2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2-[2-hydroxy-4-(2-hydroxy-3-butyloxypropoxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine,2-[2-hydroxy-4-(2-hydroxy-3-octyloxypropyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine,2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxyphenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxypropoxy)phenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1,3,5-triazine,2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine,2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hydroxypropoxy)phenyl]-1,3,5-triazine,2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine,2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,2,4-bis(4-[2-ethylhexyloxy]-2-hydroxyphenyl)-6-(4-methoxyphenyl)-1,3,5-triazine,2,4-bis(4-biphenylyl)-6-[2-hydroxy-4-(2-ethylhexyloxy)phenyl]-1,3,5-triazine.3. Metal deactivators, for example N,N′-diphenyloxamide,N-salicylal-N′-salicyloyl hydrazine, N,N′-bis(salicyloyl)hydrazine,N,N′-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hydrazine,3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyl dihydrazide,oxanilide, isophthaloyl dihydrazide, sebacoyl bi-sphenylhydrazide,N,N′-diacetyladipoyl dihydrazide, N,N′-bis(salicyloyl)oxalyldihydrazide, N,N′-bis(salicyloyl)thiopropionyl dihydrazide.4. Phosphites and phosphonites, for example triphenyl phosphite,diphenylalkyl phosphites, phenyldialkyl phosphites, tris(nonylphenyl)phosphite, trilauryl phosphite, trioctadecyl phosphite,distearylpentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl)phosphite, diisodecyl pentaerythritol diphosphite,bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite,bis(2,4-di-cumylphenyl)pentaerythritol diphosphite,bis(2,6-di-tert-butyl-4-methylphenyl)pentaerythritol diphosphite,diisodecyloxypentaerythritol diphosphite,bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite,bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite, tristearylsorbitol tri-phosphite, tetrakis(2,4-di-tert-butylphenyl)4,4′-biphenylene diphosphonite,6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenz[d,g]-1,3,2-dioxaphosphocin,bis(2,4-di-tert-butyl-6-methylphenyl)methyl phosphite,bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite,6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenz[d,g]-1,3,2-dioxaphosphocin,2,2′,2″-nitrilo[triethyltris(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite],2-ethylhexyl(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite,5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane.

The following phosphites are especially preferred:

Tris(2,4-di-tert-butylphenyl) phosphite (Irgafos® 168, Ciba SpecialtyChemicals Inc.), tris(nonylphenyl) phosphite,

5. Hydroxylamines, for example N,N-dibenzylhydroxylamine,N,N-diethylhydroxylamine, N,N-dioctylhydroxylamine,N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine,N,N-dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine,N-hexadecyl-N-octadecylhydroxylamine,N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamine derivedfrom hydrogenated tallow amine.6. Nitrones, for example, N-benzyl-alpha-phenylnitrone,N-ethyl-alpha-methylnitrone, N-octyl-alpha-heptylnitrone,N-lauryl-alpha-undecylnitrone, N-tetradecyl-alpha-tridecylnnitrone,N-hexadecyl-alpha-pentadecylnitrone,N-octadecyl-alpha-heptadecylnitrone,N-hexadecyl-alpha-heptadecylnitrone,N-ocatadecyl-alpha-pentadecylnitrone,N-heptadecyl-alpha-heptadecylnitrone,N-octadecyl-alpha-hexadecylnitrone, nitrone derived fromN,N-dialkylhydroxylamine derived from hydrogenated tallow amine.7. Thiosynergists, for example dilauryl thiodipropionate, dimistrylthiodipropionate, distearyl thiodipropionate or distearyl disulfide.8. Peroxide ccavengers, for example esters of 3-thiodipropionic acid,for example the lauryl, stearyl, myristyl or tridecyl esters,mercaptobenzimidazole or the zinc salt of 2-mercaptobenzimidazole, zincdibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritoltetrakis(β-dodecylmercapto)propionate.9. Polyamide stabilizers, for example copper salts in combination withiodides and/or phosphorus compounds and salts of divalent manganese.10. Basic co-stabilizers, for example melamine, polyvinylpyrrolidone,dicyandiamide, triallyl cyanurate, urea derivatives, hydrazinederivatives, amines, polyamides, polyurethanes, alkali metal salts andalkaline earth metal salts of higher fatty acids, for example calciumstearate, zinc stearate, magnesium behenate, magnesium stearate, sodiumricinoleate and potassium palmitate, antimony pyrocatecholate or zincpyrocatecholate.11. Nucleating agents, for example inorganic substances, such as talcum,metal oxides, such as titanium dioxide or magnesium oxide, phosphates,carbonates or sulfates of, preferably, alkaline earth metals; organiccompounds, such as mono- or polycarboxylic acids and the salts thereof,e.g. 4-tert-butylbenzoic acid, adipic acid, diphenylacetic acid, sodiumsuccinate or sodium benzoate; polymeric compounds, such as ioniccopolymers (ionomers). Especially preferred are1,3:2,4-bis(3′,4′-dimethylbenzylidene)sorbitol,1,3:2,4-di(paramethyldibenzylidene)sorbitol, and1,3:2,4-di(benzylidene)sorbitol.12. Fillers and reinforcing agents, for example calcium carbonate,silicates, surface treated silica (as described e.g. in US-A-2007/60,697and US-A-2009/111,918), glass fibres, glass beads, asbestos, talc,kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black,graphite, wood flour and flours or fibers of other natural products,synthetic fibers.13. Other additives, for example plasticisers, lubricants, emulsifiers,pigments, rheology additives, catalysts, flow-control agents, opticalbrighteners, flameproofing agents, antistatic agents and blowing agents.14. Benzofuranones and indolinones, for example those disclosed in U.S.Pat. Nos. 4,325,863; 4,338,244; 5,175,312; 5,216,052; 5,252,643;DE-A-4316611; DE-A-4316622; DE-A-4316876; EP-A-0589839, EP-A-0591102;EP-A-1291384 or3-[4-(2-acetoxyethoxy)phenyl]-5,7-di-tert-butylbenzofuran-2-one,5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phenyl]benzofuran-2-one,3,3′-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one],5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one,3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one,3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butylbenzofuran-2-one,3-(3,4-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one,3-(2,3-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one,3-(2-acetyl-5-isooctylphenyl)-5-isooctylbenzofuran-2-one.

The weight ratio of the present stabilizer composition to the totalamount of the conventional additive(s) can be for example 100:1 to1:1000 or 10:1 to 1:100 or 10:1 to 1:10.

A further embodiment of the present invention is a composition whichadditionally contains (C) an UV absorber, preferably one of those listedabove under 2.1, 2.2 or 2.8, and optionally (D) a further additiveselected from the group consisting of antioxidants, slip agents,anti-block agents, thermal fillers, pigments, anti-fog and anti-mistagents.

The weight ratio of component (A) to component (C) is for example 100:1to 1:1 or 20:1 to 3:1.

The weight ratio of Component (A) to Component (D) is for example 10:1to 1:10 or 5:1 to 1:5.

The materials stabilized according to this invention can be used in awide variety of forms, for example as films, fibres, tapes, mouldingcompositions, profiles or as binders for paints, adhesives or putties.

In more detail, the materials stabilized according to the presentinvention may be used for the preparation of the following devices:

I-1) Automotive applications, in particular bumpers, dashboards,battery, rear and front linings, moldings parts under the hood, hatshelf, trunk linings, interior linings, air bag covers, electronicmoldings for fittings (lights), panes for dashboards, headlamp glass,instrument panel, exterior linings, upholstery, automotive lights, headlights, parking lights, rear lights, stop lights, interior and exteriortrims; door panels; gas tank; glazing front side; rear windows; seatbacking, exterior panels, wire insulation, profile extrusion forsealing, cladding, pillar covers, chassis parts, exhaust systems, fuelfilter/filler, fuel pumps, fuel tank, body side mouldings, convertibletops, exterior mirrors, exterior trim, fasteners/fixings, front endmodule, glass, hinges, lock systems, luggage/roof racks, pressed/stampedparts, seals, side impact protection, sound deadener/insulator andsunroof.

I-2) Devices for plane, railway, motor car (car, motorbike) includingfurnishings.

I-3) Devices for space applications, in particular rockets andsatellites, e.g. reentry shields.

I-4) Devices for architecture and design, mining applications, acousticquietized systems, street refuges, and shelters.

II-1) Electric appliances, in particular washing machines, tumblers,ovens (microwave oven), dish-washers, mixers, and irons.

II-2) Foils for condensers, refrigerators, heating devices, airconditioners, encapsulating of electronics, semi-conductors, coffeemachines, and vacuum cleaners.

III-1) Technical articles such as cogwheel (gear), slide fittings,spacers, screws, bolts, handles, and knobs.

III-2) Rotor blades, ventilators and windmill vanes, solar devices,swimming pools, swimming pool covers, pool liners, pond liners, closets,wardrobes, dividing walls, slat walls, folding walls, roofs, shutters(e.g. roller shutters), fittings, connections between pipes, sleeves,and conveyor belts.

III-3) Profiles of any geometry (window panes) and siding.

III-4) Glass substitutes, in particular extruded plates, glazing forbuildings (monolithic, twin or multiwall), aircraft, schools, extrudedsheets, window film for architectural glazing, train, transportation,sanitary articles, and greenhouse.

III-5) Plates (walls, cutting board), extrusion-coating (photographicpaper, tetrapack and pipe coating), silos, wood substitute, plasticlumber, wood composites, walls, surfaces, furniture, decorative foil,floor coverings (interior and exterior applications), flooring, duckboards, and tiles.

III-6) Cement-, concrete-, composite-applications and covers, siding andcladding, hand rails, banisters, kitchen work tops, roofing, roofingsheets, tiles, and tarpaulins.

IV-1) Plates (walls and cutting board), trays, artificial grass,astroturf, artificial covering for stadium rings (athletics), artificialfloor for stadium rings (athletics), and tapes.

V-1) Plastic films in general (packaging, dump, laminating, swimmingpools covers, waste bags, wallpaper, stretch and shrink wrap, raffia,desalination film, batteries, and connectors).

V-2) Agricultural films (greenhouse covers, tunnel, mulch, silage, balewrap), especially in presence of intensive application ofagrochemicals).

VI-1) Food packing and wrapping (flexible and solid), BOPP, BOPET,bottles.

VI-2) Cartridges, syringes, medical applications, containers for anytransportation, waste baskets and waste bins, waste bags, bins, dustbins, bin liners, wheely bins, container in general, tanks forwater/used water/chemistry/gas/oil/gasoline/diesel; tank liners, boxes,crates, battery cases, troughs, medical devices such as piston,ophthalmic applications, diagnostic devices, and packing forpharmaceuticals blister.

VII-1) Devices of filled polymers (talc, chalk, china clay (kaolin),wollastonite, pigments, carbon black, TiO₂, mica, nanocomposites,dolomite, silica, silicates, glass, asbestos).

Thus, another embodiment of the present invention is an article made ofa composition as described above. A plastic article for agriculturaluse, preferably a thin film, typically obtained with the blow extrusiontechnology, is preferred. A monolayer film or a multi-layer film ofthree, five or seven layers is of particular interest. The mostimportant application of thin plastic films in agriculture is as coversfor greenhouses and tunnels to grow crops in a protected environment.

A multilayer film, preferably a multilayer polyolefin film, inparticular a multilayer polyethylene film, which contains a compound ofthe formula (I) in at least one layer and the compound of the formula(II) in another layer, is also preferred.

A further embodiment of the present invention is a method forstabilizing an organic material against degradation induced by light,heat or oxidation, which comprises incorporating into the organicmaterial a stabilizer composition as defined above.

A further preferred embodiment of the present invention is the use ofthe present stabilizer composition for stabilizing plastic films, inparticular polyolefin films used in agriculture and characterized byhigh levels of contamination from chemicals used in the agronomicpractice during soil disinfection and growth of the crops.

Other Embodiments of the Present Invention are

-   -   A composition containing    -   (1) a polymer selected from the group consisting of low density        polyethylene, high density polyethylene, ethylene-vinyl acetate        copolymer and ethylene-butyl acrylate copolymer, and    -   (2) a compound of the formula (II) as defined above, preferably        in a concentration of 0.005 to 5%, in particular 0.01 to 2.5% or        0.1 to 2%, relative to the weight of the polymer of component        (1).    -   A film, in particular a monolayer film or a multilayer film of        three to seven layers, made of a composition containing the        above components (1) and (2), preferably having a thickness less        than 120 microns, typically of 60 to 100 microns.    -   A method for stabilizing a polymer selected from the group        consisting of low density polyethylene, high density        polyethylene, ethylene-vinyl acetate copolymer and        ethylene-butyl acrylate copolymer, which comprises incorporating        into said polymer a compound of the formula (II) as defined        above.

The following examples illustrate the invention in greater detail. Allpercentages and parts are by weight, unless stated otherwise.

Example 1: Stabilization of LDPE (Low Density Polyethylene) Multi-LayerFilms

An appropriate amount of each formulation is weighted, containing 10% byweight in total of the light stabilizer(s) indicated in the table below,0.4% by weight of tris{2,4-di-tert-butylphenyl} phosphite and 0.1% byweight of octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate asprocess stabilizers, and the rest of polyethylene powder (PolimeriEuropa Riblene® FC 30, characterized by a density of 0.922 g/cm³ and amelt flow index (190° C./2.16 Kg) of 0.27 g/10 min). The formulationsare mixed in a turbo-mixer. Each masterbatch formulation is extruded ata maximum temperature of 200° C. in a lab-scale OMC twin-screw extruder(Ø 19 mm, L/D=25). 360 g of the granules so obtained for eachmasterbatch formulation are mixed with 30 g of a polyethylenemasterbatch containing 0.4% by weight of tris{2,4-di-tert-butylphenyl}phosphite and 0.1% by weight of octadecyl3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate as process stabilizerswith 5610 g of the above indicated virgin polyethylene in pellets, in aRhonrad® slow mixer for 10 minutes, resulting in the final formulationthat contains 0.6% in total of the light stabilizer(s) indicated in thetable below. Then, each final formulation is blown in a lab-scaleCollin® 5-layer blow-extruder (Ø20-25-30 mm, L/D 25), at a maximumtemperature of 210° C., to give a 5-layer film of overall 150 μmthickness (45-5-50-5-45 μm), having the same formulation in all layers.The following formulations are prepared:

TABLE Formulation Light stabilizer(s) 1 0.3% by weight of Stabilizer(I-1) plus 0.3% by weight of Stabilizer (II-1) 2 0.6% of Stabilizer(II-1) Stabilizer (I-1):

wherein R₁ is n-propyl and X₁ is n-butyl. Stabilizer (II-1):

wherein X₂ is n-butyl.

The testing is aimed at combining light irradiation and use ofagrochemicals known to have a detrimental effect on the light stabilityperformance of the light stabilizers contained in them. To achieve sucha purpose, an agrochemical treatment is carried out on the preparedfilms before artificial weathering. Specimens of the films for eachformulation are mounted on a small experimental greenhouse (geographicalcoordinates: Lat. 44° 25′40″N Long. 11° 16′39″E), inside of which twoburners of the type used in common agricultural practice are placed toallow sublimation of elemental sulfur, a widely used fungicide. Theso-called “sulfur burning” is carried for 13 consecutive days, 6 hoursper day, while the films are mounted on the small experimentalgreenhouse. The film specimens are covered with an additional singlepiece of opaque film to minimize the direct exposure of the sample tosunlight, in order to minimize in turn the effects of solar irradiationand hence the possible differences on samples exposed in subsequent testseries. The amount of burnt sulfur is regulated and the weatheringconditions closely monitored, so as to obtain the desired level ofcontamination from sulfur in the film samples, measured by InductivelyCoupled Plasma.

After the agrochemical treatment, the film specimens for eachformulation are exposed either in a Q-Panel QUV/se piece of equipment(QUV, as per ASTM G154, 1.55 W/m2 at 340 nm, cycle 6), or in an AtlasWeather-O-Meter (WOM, as per ASTM G155, 0.35 W/m2 at 340 nm, dry cycle),for accelerated light weathering. Specimens of the required formulationsare taken at defined intervals of time after exposure and underwenteither carbonyl increment evaluation or tensile testing. The carbonylincrement is measured by means of a Perkin-Elmer® Spectrum 100 FT-IRspectrophotometer, as a measure of the oxidation degree of the polymer;the residual tensile strength is measured, by means of a Zwick® Z1.0constant velocity tensiometer (as per modified ISO 527), in order toevaluate the decay of the mechanical properties of the plastic film, asa consequence of the polymer degradation after its oxidation.

Experiment 1

The film samples are contaminated up to an average level of sulfur of1300 ppm, then the films are exposed in the QUV and the carbonylincrement is regularly evaluated. The results are listed in Table 1.

TABLE 1 Carbonyl increment Formula- after 687 hours tion Lightstabilizer(s) exposure *⁾ 1 0.3% by weight of Stabilizer (I-1) 0.136plus 0.3% by weight of Stabilizer (II-1) 2 0.6% by weight of Stabilizer(II-1) 0.197 *⁾ Low values are desired.

Experiment 2

The film samples are contaminated up to level of sulfur of more than3000 ppm. Then, the films are exposed in the WOM and the carbonylincrement is regularly evaluated. The results are listed in Table 2.

TABLE 2 Carbonyl increment Formula- after 1402 hours tion Lightstabilizer(s) exposure *⁾ 1 0.3% by weight of Stabilizer (I-1) 0.072plus 0.3% by weight of Stabilizer (II-1) 2 0.6% by weight of Stabilizer(II-1) 0.164 *⁾ Low values are desired.

Experiment 3

The film samples are contaminated up to level of sulfur of more than3000 ppm. Then, the films are exposed in the WOM and the carbonylincrement is regularly evaluated. In this experiment samples are exposedfor tensile testing and are regularly evaluated. The results are listedin Table 3.

TABLE 3 Retained elongation at break (as % of initial) Formula- after1320 hours tion Light stabilizer(s) exposure*⁾ 1 0.3% by weight ofStabilizer (I-1) 100 plus 0.3% by weight of Stabilizer (II-1) 2 0.6% byweight of Stabilizer (II-1) 63 *⁾High values are desired.

Example 2: Stabilization of LDPE (Low Density Polyethylene) Multi-LayerFilms

An appropriate amount of each formulation is weighted, containing 10% byweight in total of the light stabilizer(s) indicated in the table below,0.4% by weight of tris{2,4-di-tert-butylphenyl} phosphite and 0.1% byweight of octadecyl 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate asprocess stabilizers, and the rest of polyethylene powder (PolimeriEuropa Riblene® FC 30, characterized by a density of 0.922 g/cm³ and amelt flow index (190° C./2.16 Kg) of 0.27 g/10 min). The formulationsare mixed in a turbo-mixer. Each masterbatch formulation is extruded ata maximum temperature of 200° C. in a lab-scale OMC twin-screw extruder(Ø 19 mm, L/D=25). 360 g of the granules so obtained for eachmasterbatch formulation are mixed with 30 g of a polyethylenemasterbatch containing 0.4% by weight of tris{2,4-di-tert-butylphenyl}phosphite and 0.1% by weight of octadecyl3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate as process stabilizerswith 5610 g of the above indicated virgin polyethylene in pellets, in aRhonrad® slow mixer for 10 minutes, resulting in the final formulationthat contains 0.6% in total of the light stabilizer(s) indicated in thetable below. Then, each final formulation is blown in a lab-scaleCollin® 5-layer blow-extruder (Ø 20-25-30 mm, L/D 25), at a maximumtemperature of 210° C., to give a 5-layer film (layers A-B-C-D-E) ofoverall 150 μm thickness (45-5-50-5-45 m for each layer respectively.The following formulations are prepared:

TABLE Formulation Light stabilizer(s) 2-1 0.3% by weight of Stabilizer(I-1) plus 0.3% by weight of Stabilizer (II-1) in all layers 2-2 0.6% ofStabilizer (II-1) in all layers 2-3 0.6% by weight of Stabilizer (I-1)in layers A-B-D-E plus 0.6% by weight of Stabilizer (II-1) in layer CStabilizer (I-1):

wherein R₁ is n-propyl and X₁ is n-butyl. Stabilizer (II-1):

wherein X₂ is n-butyl.

The testing is aimed at combining light irradiation and use ofagrochemicals known to have a detrimental effect on the light stabilityperformance of the light stabilizers contained in them. To achieve sucha purpose, an agrochemical treatment is carried out on the preparedfilms before artificial weathering. Specimens of the films for eachformulation are mounted on a small experimental greenhouse (geographicalcoordinates: Lat. 44° 25′40″N Long. 11°16′39″E), inside of which twoburners of the type used in common agricultural practice are placed toallow sublimation of elemental sulfur, a widely used fungicide. Theso-called “sulfur burning” is carried for 13 consecutive days, 6 hoursper day, while the films are mounted on the small experimentalgreenhouse. The film specimens are covered with an additional singlepiece of opaque film to minimize the direct exposure of the sample tosunlight, in order to minimize in turn the effects of solar irradiationand hence the possible differences on samples exposed in subsequent testseries. The amount of burnt sulfur is regulated and the weatheringconditions closely monitored, so as to obtain the desired level ofcontamination from sulfur in the film samples, measured by InductivelyCoupled Plasma.

After the agrochemical treatment, the film specimens for eachformulation are exposed either in a Q-Panel QUV/se piece of equipment(QUV, as per ASTM G154, 1.55 W/m2 at 340 nm, cycle 6), or in an AtlasWeather-O-Meter (WOM, as per ASTM G155, 0.35 W/m2 at 340 nm, dry cycle),for accelerated light weathering. Specimens of the required formulationsare taken at defined intervals of time after exposure and underwenteither carbonyl increment evaluation or tensile testing. The carbonylincrement is measured by means of a Perkin-Elmer® Spectrum 100 FT-IRspectrophotometer, as a measure of the oxidation degree of the polymer;the residual tensile strength is measured, by means of a Zwick® Z1.0constant velocity tensiometer (as per modified ISO 527), in order toevaluate the decay of the mechanical properties of the plastic film, asa consequence of the polymer degradation after its oxidation.

Experiment 4

The film samples are contaminated up to an average level of sulfur of1300 ppm, then the films are exposed in the QUV and the carbonylincrement is regularly evaluated. The results are listed in Table 4.

TABLE 4 Time in hours to Formula- reach 0.4 of tion Light stabilizer(s)carbonyl increment*⁾ 2-1 0.3% by weight of Stabilizer (I-1) 1152 plus0.3% by weight of Stabilizer (II-1) in all layers 2-2 0.6% by weight ofStabilizer (II-1) 833 in all layers 2-3 0.6% by weight of Stabilizer(I-1) in 931 layers A-B-D-E plus 0.6% by weight of Stabilizer (II-1) inlayer C *⁾High values are desired.

Experiment 5

The film samples are contaminated up to level of sulfur of more than3000 ppm. Then, the films are exposed in the WOM for tensile testing andare regularly evaluated. The results are listed in Table 5.

TABLE 5 Time in hours to reach 50% of the Formula- initial elongation totion Light stabilizer(s) break*⁾ 2-1 0.3% by weight of Stabilizer (I-1)2365 plus 0.3% by weight of Stabilizer (II-1) in all layers 2-2 0.6% byweight of Stabilizer (II-1) 1636 in all layers 2-3 0.6% by weight ofStabilizer (I-1) in 4112 layers A-B-D-E plus 0.6% by weight ofStabilizer (II-1) in layer C *⁾High values are desired.

The invention claimed is:
 1. A composition, containing (1) a polymerselected from the group consisting of low density polyethylene, highdensity polyethylene, ethylene-vinyl acetate copolymer andethylene-butyl acrylate copolymer, and (2) a compound of formula (II)

where radicals X₂ independently of one another are hydrogen, C₁-C₁₈alkyl, C₃-C₁₂ cycloalkyl or a group of formula (III-II)

and Y₁ is C₂-C₁₂ alkylene.
 2. A film, comprising the composition asdefined in claim
 1. 3. The film according to claim 2, which is amonolayer film or a multilayer film of three to seven layers.
 4. Amethod for stabilizing a polymer selected from the group consisting oflow density polyethylene, high density polyethylene, ethylene-vinylacetate copolymer and ethylene-butyl acrylate copolymer, the methodcomprising: incorporating into said polymer a compound of formula (II)

where radicals X₂ independently of one another are hydrogen, C₁-C₁₈alkyl, C₃-C₁₂ cycloalkyl or a group of formula (III-II)

and Y₁ is C₂-C₁₂ alkylene.